Study on flame retardant leach resistant of modified poplar wood

After flame retardant and enhancing treatment, fast-grown poplar face the problem of leaching of pharmacy, which affected the effective permanence of the retard and further use is limited. In this paper, we study the fixed effect of low molecule phenol-formaldehyde (PF) resin on nitrogen and phosphorus (N-P) inorganic flame retardant composite under the condition of high relative humidity. The change of lateral sizes and quality of the specimens were emphasized in the experiment. Results reveal that the greater the concentration of flame retardant was, the greater weight gain percentage of the samples was, and the more serious leach was in the test, after the specimen was modified with the flame retardant. When weight gain percentage of the specimens is same, the greater the concentration of PF resin test solution was, better effect of the leach resistant will be obtained with the concentration of PF test solution increased. The PF resin with 25% concentration had the best effect to reduce the leach of N-P inorganic composite retards. From the comparative analysis above, it was advisable to indicate the PF resin with 25% concentration had the best effect to reduce the leach of N-P inorganic composite retards.