Investigation the fire hazard of plywoods using a cone calorimeter

A high-efficiency fire retardant composition was prepared with dicyandiamide, phosphoric acid, boric acid, borax, urea and magnesium sulfate and it was used to process veneers which were then to prepare the plywood. Meanwhile, heat release and smoke release from combustion of plywood were tested by a cone calorimeter, including heat release rate, mass loss rate, CO yield, CO2 yield and oxygen consumption. Results showed that the plywood with this fire retardant treatment had the better flame-retardant performance and smoke suppression effect as well as the stronger char-forming capability compared to plywood without fire retardant treatment. The average heat release rate, total heat release, average effective heat of combustion, total smoke release, CO yield and oxygen consumption of the plywood with fire retardant treatment were decreased by 63.72%, 91.94%, 53.70%, 76.81%, 84.99% and 91.86%, respectively. Moreover, the fire growth index of plywood treated by fire retardant was relatively low (3.454 kW·m-2·s-1) and it took longer time to reach the peak heat release rate, accompanied with slow fire spreading. The fire performance index was relatively high (0.136 s·m2·kW-1) and it took longer time to be ignited, thus leaving a long time for escaping at fire accidents. The fire hazard of plywood with fire retardant treatment was low, and its safety level was high.

Study of nano colloidal silica sol based protectant on the prevention of masson pine

In this study, wood protectants were prepared by using manganese chloride, potassium carbonate, borax and nano colloidal silica sol. Effects of the wood protectants on decay resistance, anti-mold property and fire resistance of Pinus massoniana Lamb. were discussed. The results indicated that the optimal formula of the protectant was composed of 20% colloidal silica sol and 8% modifier (manganese chloride + potassium carbonate + borax). Under this formula, the protectant had good permeability and fluidity, accompanied with synergistic effect between colloidal silica sol and modifier. Pinus massoniana Lamb. treated by the protectant with this formula showed good decay resistance, and its mass loss rates after corrosion by Gloeophyllum trabeum and Coriolus versicolor were respectively about 21% and 19%, lower than those of the control group. This indicated that the preferred samples reached I-level decay resistance according to Chinese Forestry Industrial Standards LY/T 1283-2011. Moreover, Pinus massoniana Lamb. under this formula had good anti-mold property, manifested by 100% resistance to Aspergillus niger V. Tiegh and Trichoderma viride Pers. ex Fr. The treated Pinus massoniana Lamb. also showed good fire resistance with the oxygen indexes before and after leaching respectively at 20.45% and 13.64%, higher than those of the control group. It was concluded that the formulated protectant of this research had not only multiple functions of one dose, but also comprehensive resistances to decay, mold and fire, as well as strong leaching resistance.