The mechanical properties of CLT manufactured from densified low-density planted timber, Paraserianthes falcataria were studied in relation to changes in the area of pores for under densification. Conditioned laminas (MC ≤ 15%) underwent two-stage densification using hot-press machine at 105oC, 6 MPa, for 10 min each, with press released for 1 min 40 sec in between the stages, before cooling (< 100oC) to reduce immediate springback. The laminas with thickness 8 mm, 10 mm, and 15 mm were produced using metal stoppers and further manufactured into three-layered CLT of 24 mm, 30 mm, and 45 mm thick. 20 mm undensified laminas with 60 mm CLT as the control. Results shows that modulus of elasticity (MOE), modulus of rupture (MOR), and compression parallel to grain have improved significantly and showed negative correlation with area of pores, except for compression perpendicular to grain.