Effect of the metallization treatment on the surface properties of Populus euphratica
To improve the surface-finishing performance and enhance the protection of surface coatings, this study employed metallization treatment of fast-growing poplar through an orthogonal experiment. The poplar specimens were impregnated using a low-melting point alloy at different temperatures (75°C, 85°C, 95°C), pressures (0.5MPa, 1 MPa, 1.5 MPa), and times (0.5h, 1h, 2h) to obtain the optimum process parameters and determine the paint film adhesion of metalized poplar. The test results showed that the impregnation effect was obvious with an increase in the pressure and time. The optimum process parameters were 0.5 MPa, 85°C, and 1 h. Contact angle of the treated wood increased, the surface free energy dropped to some extent, wetting property of tread wood decreased. Whether the treated wood or the untreated wood, film adhesion of treated wood got a higher level. After anti-aging treatment, the treated poplar still had a higher level of film adhesion.