Influence of the environmental pollution on the distribution and polymerization degree of cellulose in bark and wood from scots pine (Pinus Sylvestris L.) stem
The pine stems were cut from three different polluted environments – Ist trees degradation degree (weak pollution), IInd trees degradation degree (strong pollution) and IIIrd trees degradation degree (connected with very strong pollution). On the basis of obtained results it was stated that environmental pollution caused changes in late wood participation, as well as distribution of cellulose on the stem cross- and longitudinal section. It also changed cellulose content in bark from the butt-end section, which was about 26% regardless the degradation degree. The environmental pollution caused also an increase of viscometric average polymerization degree of cellulose in heartwood in relation to heartwood adjacent sapwood and sapwood from butt-end section. Regardless the degradation degree, cellulose polymerization degree in heartwood adjacent sapwood from the middle part of the stem was higher in comparison to sapwood and heartwood. Moreover, the environmental pollution caused the increase of viscometric average polymerization degree of cellulose in bark. The polymerization degree of cellulose in bark from the butt-end section of IIIrd degradation degree stems was 22% and 23% higher in comparison to the Ist and IInd degradation degree.