WOOD RESEARCH Volume 68, Number 4, 2023
Tania Méndez-Pérez, Ma. del Carmen Chávez-Parga, Jared Maya-Alavez, Crisanto Velázquez-Becerra, Jaime Espino-Valencia, José Apolinar-Cortés, and Mauro M. Martínez-Pacheco

Stain Fungi Control in Pinus sp. Wood with Silica mesoporous Particles Loaded with Essential Oils

The use of essential oils (EO) carried onto mesoporous silica particles (MSPs) was tested to control pinewood stains. Three types of MSPs were synthesized and physicochemically characterized with N2 physisorption (type IV), X-ray diffraction [Miller indices (100), (110), (200)], scanning electron microscopy, zeta potential (negative values), dynamic light scattering (< 200 nm) and thermogravimetric analysis (5% to 10% weight loss). A response surface design was used to find the EO loading conditions to control stain, the latter was measured as colour change with the CIEDE2000 formula. The essential oil loading onto MSPC was physicochemically confirmed by a weight loss of 47% in the thermogravimetric analysis. The Citrus, Syzygium sp. and Tagetes sp. oils carried onto mesoporous particles MSPC (30:1 w/w) controlled the pinewood stain caused by Alternaria sp. and Geosmithia sp. This was demonstrated by the absence of pigmentation and scarce fungal growth.

WOOD RESEARCH Volume 62, Number 1, 2017
Ladislav Reinprecht and Zuzana Vidholdová

Growth inhibition of moulds on wood surfaces in presence of nano-zinc oxide and its combinations with polyacrylate and essential oils

The paper deals about an anti-mould efficiency of nano-zinc oxide applied into wood alone (0.1%, 0.33%, 1% and 3% ZnO) or in combination with polyacrylate (5% Paraloid B-72) and essential oils (1% and 3% clove, oregano or thyme oil). Treatment of lime tree and maple samples 50×10×5 mm (L×R×T) with these chemicals was performed by one-step or two-step dipping at 20 °C/1 h. The anti-mould efficiency of used chemicals was determined by the standard STN 49 0604 – evaluating effect of chemicals against growth of four moulds (mixture of Alternaria alternata, Aspergillus niger, Penicillium brevicompactum and Chaetomium globosum) in the 7th 14th, 21st and 28th day. The anti-mould efficiency of ZnO nanoparticles was relatively poor, however, it was evidently improved in presence of clove and oregano oils, mainly in the first 7 days of the mould test.