WOOD RESEARCH Volume 68, Number 4, 2023
Helena Hybská, Martina Mordáčová, Dagmar Samešová, and IVETA ČABALOVÁ

Ecotoxicological Tests of the Particleboards Containing Rubber Waste

The article is focused on the production and environmental evaluation of wood composites using waste rubber in the construction industry. Used aqueous extracts were prepared from the experimental wooden composites with various additions of the waste rubber from tires and waste seals. The pH value and organic pollution (by COD) were determined in the aqueous extracts. The effect on the environmental components (aquatic and terrestrial) was ecotoxicologically tested using the test organisms Sinapis alba, Lemna minor and Daphnia magna. Preliminary acute ecotoxicity tests were performed.

WOOD RESEARCH Volume 64, Number 4, 2019
Meihong Liu, Limin Peng, Zhengqiang Fan, and Dong Wang

Sound insulation and mechanical properties of wood damping composites

The sound insulation performance and mechanical properties of medium density fiberboard (MDF) and rubber multilayer panels were studied. The MDF and rubber materials were compounded under certain conditions of hot pressing, temperature and amount of glue. The weighted sound reduction was 28.0 dB for 6 mm MDF, while it was 37.4 dB for 6 mm wood composite damping material, increased by 25.1%. Compared to the monolayer MDF, the composite panels showed increased sound insulation at the resonant frequency, and the critical frequency moved to a higher frequency. The coincidence valley became shallow, effectively suppressing the anastomosis effect. As the rubber thickness increased, the multilayer composite material exhibited enhanced sound insulation efficiency and mechanical properties, and the damping properties of the composite increased, making the composite resistant to bending deformations caused by incident sound waves.