Study of dewatering characteristics of eucalyptus wood by supercritical CO2
Wood collapse is a major defect for their applications in solid wood production. Supercritical CO2 (ScCO2) dewatering can quickly remove water in wood and effectively reduce the capillary tension leading to collapse of wood structure. In this study, Eucalyptus exserta F.V. Muell wood was dewatered using ScCO2 at 35, 45, 55°C and 15, 20, 25 MPa, separately. The dewatering characteristics and wood deformation were statistically analyzed and compared after dewatering. The results show that the dewatering rate of ScCO2 is affected by moisture content (MC) of wood, showing the higher the MC, the faster the dewatering. It is also affected significantly by pressure, indicating increased dewatering rate with the pressure. The effect of temperature on dewatering rate is not apparent as the pressure is less than 25 MPa, but it becomes significant at 25 MPa condition, showing an increased dewatering rate with temperature. In this experiment, the greatest dewatering rate was 19.8%·h-1 at 55°C and 25 MPa. The transversal shrinkage of all specimens after 5 cycles dewatering was lower than 1.5%, indicating the ScCO2 dewatering could effectively inhibit collapse of eucalyptus wood structure. The transversal shrinkage decreases with the pressure, and is not affected significantly by temperature.